Effect of sample geometry on tensile properties of chomium alloyed middle carbon steel

dc.contributor.authorKučerová, Ludmila
dc.contributor.authorJeníček, Štěpán
dc.contributor.authorMach, Josef
dc.date.accessioned2019-02-04T11:00:16Z
dc.date.available2019-02-04T11:00:16Z
dc.date.issued2018
dc.description.abstract-translated42SiCr steel is a middle carbon, low alloyed steel with (in wt. %) 0.4C, 1.3Cr, 0.6Mn and 2Si. In this work, the steel was used in hot rolled state, possessing bainite-based microstructure. In development and optimization of heat and thermo-mechanical treatments, small volumes of materials are commonly processed in various simulators or dilatometers. This means that smaller samples for mechanical testing are also necessary and question arise how exactly various sample geometries affects measured mechanical properties, particularly ductility. Four types of samples for tensile test were used for the comparison. Three of them were flat, with various cross sections and active lengths of 15, 20 and 50 mm. The same thickness of 1.2 mm was kept for all three types of flat samples. For a reference, a sample with circular cross section with 5 mm diameter and 25 mm active length was tested as well. Zwick Roell Z250 was used to perform tensile tests, according to ČSN EN ISO 6892-1. Six samples of each dimension were tested and used for calculation of average values of tensile properties. Following intervals of tensile properties were obtained: yield strengths of 721-766 MPa, ultimate tensile strengths of 1205 - 1335 MPa and total elongation of 15-19%. The highest elongation was measured for circular samples, while the highest ultimate tensile strength was achieved in the flat sample with active length of 20 mm.en
dc.format5 s.cs
dc.format.mimetypeapplication/pdf
dc.identifier.citationKUČEROVÁ, L., JENÍČEK, Š., MACH, J. Effect of sample geometry on tensile propersties of chromium alloyed middle carbon steel. In: Conference Proceedings - METAL 2018 - 27th International Conference on Metallurgy and Materials. Ostrava: TANGER Ltd., Keltickova 62, 710 00 Ostrava, Czech Republic, EU, 2018. s. 761-765. ISBN 978-80-87294-84-0.en
dc.identifier.isbn978-80-87294-84-0
dc.identifier.obd43924021
dc.identifier.uri2-s2.0-85059421977
dc.identifier.urihttp://hdl.handle.net/11025/30907
dc.language.isoenen
dc.project.IDLO1502/RoRTI - Rozvoj Regionálního technologického institutucs
dc.publisherTangeren
dc.relation.ispartofseriesConference Proceedings - METAL 2018 - 27th International Conference on Metallurgy and Materialsen
dc.rightsPlný text je přístupný v rámci univerzity přihlášeným uživatelům.cs
dc.rights© Tangeren
dc.rights.accessrestrictedAccessen
dc.subject.translatedMechanical propertiesen
dc.subject.translatedsample geometryen
dc.subject.translatedchromium alloyed steelen
dc.subject.translatedmiddle carbon steelen
dc.titleEffect of sample geometry on tensile properties of chomium alloyed middle carbon steelen
dc.typekonferenční příspěvekcs
dc.typeconferenceObjecten
dc.type.statusPeer-revieweden
dc.type.versionpublishedVersionen

Files