Comparison of physical, mechanical and chemical properties of barrel steel 32CrMoV12-10 and nitriding steel 31CrMoV9 after nitriding in gas

Abstract

2CrMoV12-10 and 31CrMoV9 steels are used not only for components in the automotive industry, but also for firearms parts in the weapons industry. In these applications, high strength and surface layer hardness is required while maintaining the toughness of the core, which is achieved by nitriding. The aim of the work was to determine which of the steels exhibits better physical, mechanical and chemical properties after nitriding in a gaseous atmosphere. Metallographic samples were made to compare the structure of the nitride layer after nitriding. Hardness and fracture toughness were measured and Charpy impact testing and corrosion resistance evaluation were also carried out. The test results revealed that 31CrMoV9 steel shows better physical and chemical properties than 32CrMoV12-10 steel.

Oceli 2CrMoV12-10 a 31CrMoV9 se používají nejen na součástky v automobilovém průmyslu, ale také na díly střelných zbraní ve zbrojním průmyslu. V těchto aplikacích je vyžadována vysoká pevnost a tvrdost povrchové vrstvy při zachování houževnatosti jádra, které se dosahuje nitridací. Cílem práce bylo zjistit, která z ocelí vykazuje lepší fyzikální, mechanické a chemické vlastnosti po nitridaci v plynné atmosféře. Pro porovnání struktury nitridové vrstvy po nitridaci byly vyrobeny metalografické vzorky. Byla měřena tvrdost a lomová houževnatost a také byly provedeny Charpyho rázové zkoušky a hodnocení odolnosti proti korozi. Výsledky zkoušek odhalily, že ocel 31CrMoV9 vykazuje lepší fyzikální a chemické vlastnosti než ocel 32CrMoV12-10.